Differences observed in the surface morphology and microstructure of Ni-Fe-Cu ternary thin films electrochemically deposited at low and high applied current densities
(IOP Publishing, 2016)
In this research, nanocrystalline Ni-Fe-Cu ternary thin films using electrochemical deposition technique were produced at low and high applied current densities onto Indium Tin Oxide (ITO) coated conducting glass substrates. ...
The inﬂuence of deposit composition controlled by changing the relative Fe ion concentration on properties of electroplated nanocrystalline Co-Fe-Cu ternary thin ﬁlms
Ternary Co-Fe-Cu thin ﬁlms with 78.5–92.4 at.% Co, 4.1–17.9 at.% Fe, and 3.1–3.6 at.% Cu were electroplated at ambient temperature from electrolytes with diﬀerent relative Fe ion concentrations with respect to the Co ion ...
Differences observed in the phase structure, grain size–shape, and coercivity field of electrochemically deposited ni–co thin films with different co contents
Nanostructured Ni–Co thin films were produced using galvanostatic electrodeposition on indium tin oxide (ITO)-coated glass substrates from an aqueous electrolyte solution without stirring at ambient temperature. Different ...
Evolution of surface roughness parameters and microstructure in two-phase nanocrystalline Co–Cu ﬁlms electrodeposited onto ITO coated glass substrates at different deposition potentials
In the present research, we have studied the effect of deposition potential on the ﬁlm composition, structural, and morphological properties of the electrodeposited Co–Cu thin ﬁlms grown onto indium tin oxide coated glass ...
An investigation of structural properties and surface morphologies of electrochemically fabricated nanocrystalline Ni–Co–Cu/ITO deposits with different compositions
In this study, nanocrystalline ternary Ni–Co–Cu/ITO deposits with different compositions were produced by using the electrochemical deposition technique from a sulfate-based bath solution with different Co ion concentrations. It ...
A comparative study on microstructures, magnetic features and morphologies of ternary fe–co–ni alloy thin films electrochemically fabricated at different deposition potentials
(Journal of Superconductivity and Novel Magnetism, 2019)
Electrochemically fabricated ternary Fe–Co–Ni alloy thin films with different chemical compositions were obtained at different deposition potentials. An increase in the deposition potential increased the Ni content while ...