Thermowood metodu ile ısıl işlem görmüş İsveç çamı, Sibirya çamı ve sarıçam odunlarında bazı yüzey özelliklerinin belirlenmesi

Abstract

In this study, it is aimed to determine the values of the color (L*, a*, b*, ΔL*, Δb*, Δa*ve ΔE*) values and perpendicular and parallel glossiness values of define according to the ThermoWood method heat treated at 212oC for 1 and 2 hours and untreatment lodgepole pine (Pinus contorta), siberian pine (Pinus sibiric) and scots pine (Pinus sylvestris L.) wood materials. For this purpose, in the tests made after heat treatment application, changes in color and glossiness have also been found to be effective. For all wood types, it was determined that the total color difference (ΔE*) values increased and the L* values decreased due to the increase in heat treatment time. It was observed that the values of perpendicular and parallel glossiness measured at 20o, 60o and 85o were changed depending on the increase of heat treatment time.

Bu çalışmada, ThermoWood metoduna göre belirtilen 212oC’de 1 ve 2 saat süre ile ısıl işlem muameleleri görmüş ve görmemiş İsveç çamı (Pinus contorta), Sibirya çamı (Pinus sibiric) ve sarıçam (PinussylvestrisL.) ahşap malzemeler üzerinde renk (L*, a*, b*, ΔL*, Δb*, Δa* ve ΔE*) değerleri ile yüzeye dik ve paralel parlaklık değerlerinin tespit edilmesi amaçlanmıştır. Bu amaç ile ısıl işlem uygulamasından sonra yapılan testlerde renk ve parlaklık değişimlerinde sürenin etkili olduğu ortaya çıkmıştır. Bütün ağaç türleri içinde ısıl işlem süresinin artmasına bağlı olarak toplam renk farkı (ΔE*) değerlerinin arttığı, L* değerlerinin azaldığı belirlenmiştir.Ayrıca 20o, 60ove 85o’de ölçülen liflere dik ve paralel parlaklık değerlerinin ısıl işlem süresinin artmasına bağlı olarak değiştiği de görülmüştür.