dc.identifier.citationYılmaz, H. (2017). Rwat (Rubber wheel abrasion test) yöntemi ile endüstriyel atıkların Al 6061 üzerindeki aşındırma davranışlarının incelenmesi. Yayımlanmamış yüksek lisans tezi. Bartın: Bartın Üniversitesi Fen Bilimleri Enstitüsüen_US
dc.identifier.urihttp://hdl.handle.net/11772/420
dc.description.abstractBu çalışmada, ham demir, çelik ve ferrokrom cevheri üretiminde endüstriyel atık olarak ortaya çıkan cürufların aşındırıcı özellikleri araştırılmıştır. Deneylerde yüksek fırın cürufu (YFC), Çelikhane cürufu (ÇC) ferrokrom cürufu (FKC) ve ticari Al2O3 tozları kullanılmıştır. Aşınma testleri Rubber Whell Abbrasion Wear (RWAT) yöntemi ile gerçekleştirilmiştir. Karşı yüzey malzemesi olarak Al 6061 seçilmiştir. Testler, 25, 50, 75 ve 100 N luk yükler altında 100 d/dk Rubber Whell dönme hızında gerçekleştirilmiştir. Yapılan deneysel çalışmalar sonucunda en yüksek aşındırıcılık oranı uygulanan tüm yüklerde YFC cürufunda görülmüştür. Yüksek yüklerde FKC nin aşındırma performansı ticari Al2O3 yetişmiştir. ÇC nun aşındırıcı özelliğinin olmadığı anlaşılmıştır. Aşındırma performansnda partikül sertliği kadar yüzey morfolojisi ve SPQ (spike parameter–quadratic fit) değerinin önemli olduğu anlaşılmıştır. Aşınma mekanizması olarak YFC ve Al2O3 aşındırılan numunelerde spalling, ploughing ve mikro çizilme görülürken, FKC de malzemenin aşırı plastik deformasyona bağlı ekstrüzyona uğradığı görülmüştür.en_US
dc.description.abstractIn this study, the abrading characteristics of the industrial slags, generated in the form of industrial waste during raw iron, steel and ferrochromium ore production, are investigated. Granulated blast furnace slag (GBFS), basic oxygen furnace slag (BOFS) ferrochromium slag (FCS) and commercial Al2O3 powder were used during the tests. Abrasion tests were conducted using Rubber Wheel Abrasion Wear (RWAT) method. Al 6061 was chosen as the counter body material. The tests were conducted under 25, 50, 75 and 100 N loads with 100 r/min rubber wheel rotational speed. The highest rate of abrasion was obtained from GBFS under all loads as a result of the conducted tests. Under high loads, the abrading performance of FCS reached that of the commercial Al2O3 powder. BOFS was found to have no abrading capability. Surface morphology and SPQ (spike parameter-quadratic fit) value were as effective as the particle hardness in the evaluation of abrading performance. As dominant wear mechanisms, spalling, ploughing and micro-scratch formation were observed on the specimens abraded with GBFS and Al2O3, whereas severe plastic deformation-induced extrusion was observed on the specimen abraded with FCS.en_US
dc.language.isoturen_US
dc.publisherBartın Üniversitesi,Fen Bilimleri Enstitüsüen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectMühendisliken_US
dc.subjectEndüstriyel atıken_US
dc.subjectMalzeme bilimien_US
dc.subjectEngineeringen_US
dc.subjectIndustrial wasteen_US
dc.subjectMaterial scienceen_US
dc.titleRwat (Rubber wheel abrasion test) yöntemi ile endüstriyel atıkların Al 6061 üzerindeki aşındırma davranışlarının incelenmesien_US
dc.title.alternativeInevestigation of abrasive wear behavior of industrial wastes on Al 6061 material using rubber wheel abrasion test (RWAT)en_US
dc.typemasterThesisen_US
dc.contributor.departmentBartın Üniversitesi, Fen Bilimleri Enstitüsü,Makine Mühendisliği Anabilim Dalıen_US


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record