Effects of Glues Modified with Borax on the Bonding Strength Of Chestnut Wood

Abstract

In this study, the effects of polivinalacetat (PVAc), ure-formaldehyd (UF), polyuretan (PU) glues and theirmodification with borax on bonding resistance of chestnut (Castenea sativa Mill.) wood in the Agean Regionwere evaluated. For this purpose, the samples prepared from chestnut (Castenea sativa Mill.) woods obtainedfrom Simav in Agean Region were glued with Polivinalacetat (PVAc), Ure-formaldehyd (UF), Polyuretan (PU)glues and with modifications of these glues, PVAc + %5 Boraks, UF + %5 Boraks, PU + %5 Boraks. Thesamples prepared through this process were subjected to tension test according to DIN 53255 standarts.Based on initial results, the best glued resistance was obtained with the samples glued with UF glue (8,59N/mm²), the worst resistance was obtained with the samples attached with PU + %5 Boraks (2,50 N/mm²).Bu çalışmada, polivinilasetat (PVAc), üre-formaldehit (UF), poliüretan (PU), tutkallarının ve bu tutkallarınboraks ile karışımının İç Ege Bölgesi'nde yetişen kestane (Castenea sativa Mill.) odununun yapışma direncineetkileri incelenmiştir. Bu amaçla, İç Ege Bölgesi'nde Simav Yöresi'nde yetişen kestane (Castenea sativa Mill.)odunundan hazırlanan deney örnekleri polivinilasetat (PVAc), üre- formaldehit (UF), Poliüretan(PU), tutkallarıve PVAc + %5 Boraks, UF+ %5 Boraks, PU + %5 boraks karışımlarıyla elde edilen tutkallarla yapıştırılmıştır.Hazırlanan deney örnekleri DIN 53255 esaslarına göre çekme direnci deneyine tabi tutulmuştur.Sonuç olarak; en yüksek yapışma direnci Üre-formaldehit tutkalı ile yapıştırılmış örneklerde 8.59 N/mm², endüşük yapışma direnci ise % 5 oranında modifiye edilmiş poliüretan tutkalı ile yapıştırılmış örneklerde 2.50N/mm² olarak elde edilmiştir.