Vacuum-heat treatment of Scots pine (Pinus sylvestris L.) wood pretreated with propanetriol

Abstract

Scots pine sapwood was pretreated with two levels of propanetriol (20% and 40% w/w glycerol), and then subjected to vacuum-heat treatment (VHT) at 180 degrees C and 200 degrees C. The treated samples were examined with respect to their weight and volumetric changes, mechanical properties, colour changes, and dynamic water vapour sorption. The weight of the samples after VHT did not change with increasing the temperature, but it was increased in glycerol pretreated samples. Combination of glycerol pretreatment and VHT decreased the maximum swelling. Total colour change was significantly higher during VHT at a higher temperature, while no obvious trend observed in the samples pretreated with glycerol. Modulus of elasticity (MOE) and modulus of rupture (MOR) were not affected by solely VHT, but strongly decreased after glycerol pretreatment. The equilibrium moisture content (EMC) of the samples decreased by VHT. The glycerol pretreatment caused a reduction in EMC values at a relative humidity (RH) below 60%, but considerably increased the moisture sorption in the RH above 75%. VHT slightly reduced the sorption hysteresis compared to untreated wood, but an apparent reduction in hysteresis observed by glycerol pretreatment. This indicates that the flexibility of the wood cell wall polymers increases due to glycerol pretreatment, which results in decreased MOE and sorption hysteresis values.