EFFECTS OF PRESSURE AND TEMPERATURE ON PHYSICAL AND MECHANICAL PROPERTIES OF HIGH DENSITY FIBERBOARD

Abstract

In this study, high density fiberboard was manufactured by using dry process. The effects of press temperatureand pressure on physical and mechanical properties were investigated. The fibers were obtained from SFC MDFmill consisting of 70% Pinus spp. and 30% hardwoods. The laboratory conditions were as fallows; prestemperatures were 160-170-180-190 °C, pressure as 50-55 kg/cm2, total pressing time as 100 seconds. The HDFproduced had 5±0,2 mm and having the density of 1,02-1,12 g/cm3. The physical and mechanical properties ofthe panels were determined according to TS EN standards. It was found that increasing temperature and pressurehad positive effect on the properties.Bu araştırmada, Kuru Yöntemle sert lif levha üretilmiştir. Üretim koşullarından pres sıcaklığı ve basıncınınlevhaların fiziksel ve mekanik özellikleri üzerine etkisi araştırılmıştır. Lifler; Kastamonu SFC A.Ş.'den teminedilmiş olup, %70 çam türleri, %30 yapraklı ağaç türleri karışımından oluşmaktadır. Laboratuar koşullarında160-170-180-190 °C sıcaklık ve 50-55 kg/cm2 pres basıncı, 100 sn toplam pres süresi kullanılarak 5±0,2 mmkalınlığında ve 1,02-1,12 g/cm3 özgül kütleli sert lif levhalar elde edilmiştir. Levhaların fiziksel ve mekaniközellikleri, TS EN standartları kullanılarak belirlenmiştir. Bu çalışmada sıcaklık ve basınç artışının levhalarınfiziksel ve mekanik özelliklerini olumlu yönde etkilediği tespit edilmiştir.