Effect of Bismuth on hydrogen storage properties of melt-spun LaNi4.7-x Al0.3Bix (x = 0.0, 0.1, 0.2, 0.3) ribbons

Abstract

The LaNi5 intermetallic compound is an AB5 type hydrogen storage alloy which exhibits low operating temperature, easy activation, low pressure and tolerance to impurities. In this study, LaNi4.7-x Al0.3Bix (x = 0.0, 0.1, 0.2, 0.3) alloys were produced by melt-spinning technique and the effects of Al and Bi additions on the microstructure, thermal and hydrogen storage properties of LaNi5 were investigated. The results showed that substitution of Ni with Al led to a desired decrease in absorption/desorption plateau pressure and hysteresis without a decrease in hydrogen storage capacity. In contrast, Bi substitution with Ni increased the absorption/desorption plateau pressure, reduced the hydrogen capacity and increased pulverization resistance of the alloy due to the formation of BiLa and AlNi3 intermetallic phases at the grain boundaries.