Effects of Cellulose Micro and Nanocrystals on the Mechanical, Thermal, Morphological, and Structural Properties of Rigid Polyurethanes

Abstract

Effects of adding microcrystalline cellulose (MCC) and cellulose nanocrystals (CNC) were evaluated relative to the mechanical, thermal, morphological, and structural properties of rigid polyurethanes (rPUs). The composites were prepared with the blending of polyols/isocyanates and the cellulosic fillers at 0.25%, 0.5%, and 1% loadings. Scanning electron microscopic images showed that the samples had micro -scaled porosity, with cell sizes ranging from 250 to 800 nm. The fillers improved the mechanical strengths and modulus of neat rPUs due to the presence of the nano -sized cells in rPUs matrix. The addition of both fillers generally did not provide a positive effect on the thermal properties, and the weight loss generally increased while the loading rate of the fillers was increased from 0.25% to 1%. The samples had two small crystalline peaks at 18 degrees and 19 degrees according to the X-ray diffraction analysis. From the results, it can be said that the presence of both fillers generally improved all properties of the neat rPUs, and the effects of CNC on the properties were higher than MCC due to both lower particle size and the higher crystallinity of CNC.