Effect of Multilayer Nanocomposite TiAlSiN/TiSiN/TiAlN Coating on Wear Behavior of Carbide Tools in the Milling of Hardened AISI D2 Steel

Abstract

Thin hard coatings are widely used in the protection of cutting tools, dies and molds to prolong their wear resistance and lifetime. Superior properties of different coatings can be combined with multilayer design, and especially a higher microhardness can be obtained by nanocomposite structures. In this study, a multilayer design composing of TiAlSiN, TiSiN and TiAlN layers was applied on carbide cutting tools. The top TiAlSiN layer has a nanocomposite structure of crystalline fcc-TiAlN and amorphous Si3N4 phases. The multilayer nanocomposite TiAlSiN/TiSiN/TiAlN coating was deposited on the carbide cutting tool using an industrial magnetron sputtering system. Wear behavior of the coated tools was investigated in the milling of hardened AISI D2 steel (similar to 55 HRc). The changes in tool wear and surface roughness as a function of cutting distance were recorded. Wear mechanisms and types were investigated using optical and scanning electron microscopy in combination with energy dispersive spectroscopy. It was found that the multilayer nanocomposite TiAlSiN/TiSiN/TiAlN coating provides at least 1.2 times higher wear resistance and a longer lifetime than single layer TiN and TiAlN coatings. Main wear mechanisms are abrasion and adhesion of the workpiece material on the cutting edge. As a result, wear types are notch wear and build-up-edge formation.