The Determination of Effec of Finishing on The Thermal Conductivity of Impregnated Scotch Pine

Abstract

Wood material has used as construction material in many interior and outdoor areas. The aim of this study; to specify effects of wood material (Scotch Pine) impregnated by borax, zinc chloride, boric acid and ammonium sulfate by applying and two type impregnation methods (dipping and pressure), finished with some varnishes (synthetic,polyurethane,cellulosic) and different paints (industrial cellulosic, synthetic, cellulosic) on thermal conductivity. Thermal conductivity test was applied according to ASTM C 1113-99. As a results, observed that impregnation materials increased on thermal conductivity. The founded that the lowest thermal counductivity of 0.117 (Kcal / mh°C) from scotch pine control samples. In addition the highest value thermal conductivity of 0.143 (Kcal/mh°C) was aquired from scotch pine application finished and industrial painted impregnated by boric acid chemical applying pressure method.Ağaç malzeme iç ve dış mekânda bir çok alanda yapı malzemesi olarak kullanılmaktadır. Bu çalışmanın amacı, yangın geciktirici özelliğe sahip olan; boraks, çinko klorür, borik asit ve amonyum sülfat ile 2 çeşit empreyne yöntemi (daldırma, basınç) uygulanarak emprenye edilen sarıçam ağaç malzeme üzerine farklı üst yüzey vernikleri (sentetik, poliüretan, selülozik,) ve boyaları (endüstriyel selülozik, sentetik, selülozik,) uygulanarak ısı iletkenliğine etkisini belirlemektir. Isı iletkenliği testi ASTM C 113-99 standardında belirtilen özelliklere göre uygulanmıştır. Sonuç olarak, kullanılan emprenye maddelerinin ısı iletkenliğini düşürdüğü görülmüştür. Isı iletkenliği katsayısı en düşük 0.117 (kcal /mh°C) olarak sarıçam kontrol örneklerinde bulunmuştur. Isı iletkenlik katsayısı en yüksek 0.143(kcal/mh°C) olarak basınç yöntemi uygulanarak borik asit emprenyeli sarıçam örneklerinden elde edilmiştir.