Thermowood metoduna göre ısıl işlem görmüş santos, gül ve üvez odunlarında renk ve parlaklık özelliklerinin belirlenmesi
Özet
In this research, it was aimed to determine the
glossiness and color properties of the santos
(Myroxylon balsamum), rose (Dalbergia nigra) and uvez
(Sorbus L.) woods which were heat treated according
to ThermoWood method. For this purpose, according to
the ThermoWood method, the samples were subjected
to heat treatment at 212°C for 1 and 2 hours. Values of
color and glossiness values were determined on the
heat treated and untreated materials. L* value is
decreased due to the increase of the heat treatment
time. while the highest ΔE* value was obtained on heat
treated rowan wood at 212°C for 2 hours, the lowest
ΔE* value was found on heat treated santos wood at
212°C for 1 hour. When the highest perpendicular and
paralel glossiness values at 20o were obtained on
control rowan wood, the highest perpendicular and
paralel glossiness values at 60o and 85o on heat treated
rose wood at 212°C for 1 hour. Bu araştırmada, ThermoWood metoduna göre ısıl işlem görmüş santos (Myroxylon balsamum), gül (Dalbergia nigra) ve üvez (SorbusL.) odunlarında meydana gelen parlaklık ve renk özelliklerinin belirlenmesi amaçlanmıştır. Bu amaç ile test örneklerine, ThermoWood metoduna göre 212oC’de 1 ve 2 saat süre ile ısıl işlem uygulanmıştır. Isıl işlem görmüş ve görmemiş malzemeleri üzerinde renk ve parlaklık değerleri belirlenmiştir. Isıl işlem süresinin artmasına bağlı olarak L* değerinin azaldığı görülmektedir. En yüksek ΔE* değeri 212oC’de 2 saat süreyle ısıl işlem uygulanmış üvez odununda, en düşük ΔE* değeri ise 212oC’de 1 saat süreyle ısıl işlem uygulanmış santos odununda ortaya çıkmıştır. En yüksek 20o’de liflere dik ve paralel parlaklık değerlerinde üvez odununa ait kontrol örneklerinde elde edilirken, 60o ve 85o’de liflere dik ve paralel değerlerinde ise 212oC’de 1 saat süreyle ısıl işlem uygulan gül ağacında elde edilmiştir.