dc.description.abstractFe-Cu films with low and high Fe : Cu ratio have been produced from the electrolytes with different Fe ion concentrations at aconstant deposition potential of−1400 mV versus saturated calomel electrode (SCE) by electrodeposition technique onto indiumtin oxide (ITO) coated conducting glass substrates. It was observed that the variation of Fe ion concentration in the electrolytehad a very strong influence on the compositional, surface morphological, and microstructural properties of the Fe-Cu films. Anincrease in the Fe ion concentration within the plating bath increased the Fe content, consequently Fe : Cu ratio within the films.The crystallographic structure analysis showed that the Fe-Cu films had a mixture of face-centered cubic (fcc) Cu and body centeredcubic (bcc) ----Fe phases. The average crystallite size decreased with the Fe ion concentration. The film electrodeposited from theelectrolyte with low Fe ion concentration exhibited a morphology consisting of dendritic structures. However, the film morphologychanged from dendritic structure to cauliflower-like structure at high Fe ion concentration. The surface roughness and grain sizewere found to decrease significantly with increasing Fe ion concentration in the electrolyte. The significant differences observed inthe microstructural and morphological properties caused by the change of Fe ion concentration in the electrolyte were ascribed tothe change of Fe : Cu ratio within the filmsen_US
dc.language.isoengen_US
dc.publisherHindawi Publishing Corporationen_US
dc.relation.isversionofhttp://dx.doi.org/10.1155/2013/971790en_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectSEMen_US
dc.subjectFe-Cu thin filmsen_US
dc.titleComparison of microstructural and morphological properties of electrodeposited Fe-Cu thin films with low and high Fe : Cu ratioen_US
dc.typearticleen_US
dc.relation.journalAdvances in Materials Science and Engineeringen_US
dc.contributor.departmentBartın Üniversitesi, Eğitim Fakültesi, Matematik ve Fen Bilimleri Eğitimi Bölümüen_US
dc.identifier.startpage1en_US
dc.identifier.endpage7en_US


Bu öğenin dosyaları:

Thumbnail

Bu öğe aşağıdaki koleksiyon(lar)da görünmektedir.

Basit öğe kaydını göster